We have measured the transformation of pseudomorphic Ni films on Pd(100) into their bulk fcc phase as a function of the film thickness. We made use of x-ray diffraction and x-ray induced photoemission to study the evolution of the Ni film and its interface with the substrate. The growth of a film with tetragonally strained face centered symmetry (fct) has been observed by out-of-plane x-ray diffraction up to a limit thickness of 10 Ni pseudomorphic layers (some of them partially filled and intermixed with the substrate), where a new fcc bulklike phase is formed. After the formation of the bulklike Ni domains, we observed the pseudomorphic fct domains to disappear preserving the number of layers and their spacing. The phase transition thus proceeds via lateral growth of the bulklike phase within the pseudomorphic one, i.e., the bulklike fcc domains penetrate down to the substrate when formed. This large depth of the walls separating the domains of different phases is also indicated by the increase of the intermixing at the substrate-film interface, which starts at the onset of the transition and continues at even larger thickness. The bulklike fcc phase is also slightly strained; its relaxation towards the orthomorphic lattice structure proceeds slowly with the film thickness, being not yet completed at the maximum thickness presently studied of 30 Angstrom (similar to17 layers).

Pseudomorphic to bulk fcc phase transition of thin Ni films on Pd(100)

A. COSSARO;MORGANTE, ALBERTO;
2004-01-01

Abstract

We have measured the transformation of pseudomorphic Ni films on Pd(100) into their bulk fcc phase as a function of the film thickness. We made use of x-ray diffraction and x-ray induced photoemission to study the evolution of the Ni film and its interface with the substrate. The growth of a film with tetragonally strained face centered symmetry (fct) has been observed by out-of-plane x-ray diffraction up to a limit thickness of 10 Ni pseudomorphic layers (some of them partially filled and intermixed with the substrate), where a new fcc bulklike phase is formed. After the formation of the bulklike Ni domains, we observed the pseudomorphic fct domains to disappear preserving the number of layers and their spacing. The phase transition thus proceeds via lateral growth of the bulklike phase within the pseudomorphic one, i.e., the bulklike fcc domains penetrate down to the substrate when formed. This large depth of the walls separating the domains of different phases is also indicated by the increase of the intermixing at the substrate-film interface, which starts at the onset of the transition and continues at even larger thickness. The bulklike fcc phase is also slightly strained; its relaxation towards the orthomorphic lattice structure proceeds slowly with the film thickness, being not yet completed at the maximum thickness presently studied of 30 Angstrom (similar to17 layers).
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11368/1697104
 Avviso

Registrazione in corso di verifica.
La registrazione di questo prodotto non è ancora stata validata in ArTS.

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 10
  • ???jsp.display-item.citation.isi??? 10
social impact