During the curing reaction, the monomers of dentine bonding systems should crosslink sufficiently to strengthen an adhesive so that it is clinically reliable. This study evaluated how different storage conditions (air vs. water storage) affect the elastic modulus (E-modulus) and degree of conversion (DC) of a three-step etch-and-rinse adhesive and a two-step self-etch adhesive. The biaxial flexural test and Raman microscopy were performed on resin disks made from the bonding agents Adper Scotchbond Multi-Purpose (SBMP; 3M ESPE) and Clearfil Protect Bond (CPB; Kuraray). The measurements were repeated after storage in either air or water for 15 and 30 min and for 1, 24, and 72 h. At time 0, the E-modulus was not affected by the adhesive system, whilst the degree of cure of CPB was higher than that of SBMP. Air storage increased the E-modulus at each ageing interval. Storage in water increased the E-modulus until it reached a maximum at 24 h, after which it decreased significantly at 72 h. No linear correlation between the percentage DC and E-modulus of the two adhesives was found when stored in water. The results of this study indicate that the mechanical properties and polymerization kinetics of SBMP and CPB are affected by storage time and medium.

The effect of ageing on the elastic modulus and degree of conversion of two multistep adhesive systems

MARCHESI, GIULIO;NAVARRA, CHIARA;CADENARO, MILENA;CODAN, BARBARA;SERGO, VALTER;DI LENARDA, Roberto;BRESCHI, LORENZO
2010-01-01

Abstract

During the curing reaction, the monomers of dentine bonding systems should crosslink sufficiently to strengthen an adhesive so that it is clinically reliable. This study evaluated how different storage conditions (air vs. water storage) affect the elastic modulus (E-modulus) and degree of conversion (DC) of a three-step etch-and-rinse adhesive and a two-step self-etch adhesive. The biaxial flexural test and Raman microscopy were performed on resin disks made from the bonding agents Adper Scotchbond Multi-Purpose (SBMP; 3M ESPE) and Clearfil Protect Bond (CPB; Kuraray). The measurements were repeated after storage in either air or water for 15 and 30 min and for 1, 24, and 72 h. At time 0, the E-modulus was not affected by the adhesive system, whilst the degree of cure of CPB was higher than that of SBMP. Air storage increased the E-modulus at each ageing interval. Storage in water increased the E-modulus until it reached a maximum at 24 h, after which it decreased significantly at 72 h. No linear correlation between the percentage DC and E-modulus of the two adhesives was found when stored in water. The results of this study indicate that the mechanical properties and polymerization kinetics of SBMP and CPB are affected by storage time and medium.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11368/2296921
 Avviso

Registrazione in corso di verifica.
La registrazione di questo prodotto non è ancora stata validata in ArTS.

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? 12
social impact