Purpose: To assess the degree of conversion (DC) at different levels of a resin-based luting agent used with different commercial posts. METHODS: A resin-based luting agent (Variolink II) was light-cured in a simulated dowel space in combination with different fiber posts: GC Fiber Post (GC), DT Light Safety Lock (SL), RelyX Fiber Post (RX), Reforpost (RE), DT Light Post Illusion (LPI), FRC Postec Plus (FP), Radix (RA), Snowpost (SP), Dentin Post X (DP), Macrolock Illusion (MI), and Composipost (CP). After 24 hours, DC was assessed through micro-Raman analysis at the coronal, middle, and apical thirds. Two-way ANOVA and Tukey test were used for post-hoc comparisons (P<0.05). RESULTS: The results demonstrated that the post-type, dowel space level, and between-factor interaction were statistically significant (P<0.001). Differences in DC were observed at different depths for RX, RE, LPI, SL, DP, MI and CP, decreasing from the coronal to the apical third. Although the resin-based luting agent should be able to polymerize in absence of light, a higher DC was found following light irradiation (with a decreasing effect from the coronal to the apical third).

Influence of post type on degree of conversion of a resin-based luting agent.

NAVARRA, CHIARA;BRESCHI, LORENZO;CADENARO, MILENA;
2012-01-01

Abstract

Purpose: To assess the degree of conversion (DC) at different levels of a resin-based luting agent used with different commercial posts. METHODS: A resin-based luting agent (Variolink II) was light-cured in a simulated dowel space in combination with different fiber posts: GC Fiber Post (GC), DT Light Safety Lock (SL), RelyX Fiber Post (RX), Reforpost (RE), DT Light Post Illusion (LPI), FRC Postec Plus (FP), Radix (RA), Snowpost (SP), Dentin Post X (DP), Macrolock Illusion (MI), and Composipost (CP). After 24 hours, DC was assessed through micro-Raman analysis at the coronal, middle, and apical thirds. Two-way ANOVA and Tukey test were used for post-hoc comparisons (P<0.05). RESULTS: The results demonstrated that the post-type, dowel space level, and between-factor interaction were statistically significant (P<0.001). Differences in DC were observed at different depths for RX, RE, LPI, SL, DP, MI and CP, decreasing from the coronal to the apical third. Although the resin-based luting agent should be able to polymerize in absence of light, a higher DC was found following light irradiation (with a decreasing effect from the coronal to the apical third).
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11368/2550818
 Avviso

Registrazione in corso di verifica.
La registrazione di questo prodotto non è ancora stata validata in ArTS.

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? 6
social impact