We have successfully grown regular arrays of InAs/GaAs quantum dots on patterned Si substrates. Thanks to the capability of nanopimprint lithography, we were able to obtain uniform patterns extended over some cm2 areas, with periods of 300nm. Ex-situ and in-situ treatments of the surface allowed us to completely remove any residual oxides prior to growth without the use of hydrogen beams, at temperatures compatible with standard III-V molecular beam epitaxy. The growth protocol was optimized in order to obtain a perfect selectivity of InAs/GaAs nanostructures in the holes, without any deposition on the planar areas.
III-V site-controlled quantum dots on Si patterned by nanoimprint lithography
HUSSAIN, SAJID;ZANNIER, VALENTINA;
In corso di stampa
Abstract
We have successfully grown regular arrays of InAs/GaAs quantum dots on patterned Si substrates. Thanks to the capability of nanopimprint lithography, we were able to obtain uniform patterns extended over some cm2 areas, with periods of 300nm. Ex-situ and in-situ treatments of the surface allowed us to completely remove any residual oxides prior to growth without the use of hydrogen beams, at temperatures compatible with standard III-V molecular beam epitaxy. The growth protocol was optimized in order to obtain a perfect selectivity of InAs/GaAs nanostructures in the holes, without any deposition on the planar areas.File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.