The aim of this study was to analyze the extent of polymerization of different adhesive systems on whitened dentin. One adhesive of each class was investigated: Adper Scotchbond Multi Purpose (3M ESPE); One-Step (Bisco); Clearfil Protect Bond (Kuraray); and Xeno III (Dentsply DeTrey). Dentin disks were treated with Opalescence Xtra Boost (Ultradent) for 30 min and bonded immediately after 24 h or after 14 d of storage in 100% humidity at 37°C. Unbleached dentin disks were prepared as controls. The extent of polymerization of bonded interfaces was obtained with differential scanning calorimetry (DSC) at 20, 40 and 60 s, and the data were statistically analyzed. The extent of polymerization obtained from DSC exotherms of adhesives applied immediately after whitening was significantly lower compared with controls. An increased extent of polymerization after storage was confirmed for all adhesives, and no difference with controls was found after 14 d. A prolonged irradiation time increased
Influence of whitening on the degree of conversion of dental adhesives on dentin.
CADENARO, MILENA;BRESCHI, LORENZO;ANTONIOLLI, FRANCESCA;DI LENARDA, Roberto
2006-01-01
Abstract
The aim of this study was to analyze the extent of polymerization of different adhesive systems on whitened dentin. One adhesive of each class was investigated: Adper Scotchbond Multi Purpose (3M ESPE); One-Step (Bisco); Clearfil Protect Bond (Kuraray); and Xeno III (Dentsply DeTrey). Dentin disks were treated with Opalescence Xtra Boost (Ultradent) for 30 min and bonded immediately after 24 h or after 14 d of storage in 100% humidity at 37°C. Unbleached dentin disks were prepared as controls. The extent of polymerization of bonded interfaces was obtained with differential scanning calorimetry (DSC) at 20, 40 and 60 s, and the data were statistically analyzed. The extent of polymerization obtained from DSC exotherms of adhesives applied immediately after whitening was significantly lower compared with controls. An increased extent of polymerization after storage was confirmed for all adhesives, and no difference with controls was found after 14 d. A prolonged irradiation time increasedPubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.