A comparison of the corrosion resistance of AA6060T5 and AA6082T6 jointed surfaces via Friction StirWelding (FSW) and Metal Inert Gas (MIG), respectively, is reported. The test was conducted putting the welded and polished samples in an acid salt solution. The corrosion resistance was detected via morphological analysis of the surface. The attack was localized (pitting), an index referred to the pit density was used for the comparison. The result indicated that the joint welded via Friction Stir is more resistant than that welded via Metal Inert Gas technique.

Corrosion resistance in FSW and in MIG welding techniques of AA6XXX

MAGGIOLINO, STEFANO;SCHMID, CHIARA
2008-01-01

Abstract

A comparison of the corrosion resistance of AA6060T5 and AA6082T6 jointed surfaces via Friction StirWelding (FSW) and Metal Inert Gas (MIG), respectively, is reported. The test was conducted putting the welded and polished samples in an acid salt solution. The corrosion resistance was detected via morphological analysis of the surface. The attack was localized (pitting), an index referred to the pit density was used for the comparison. The result indicated that the joint welded via Friction Stir is more resistant than that welded via Metal Inert Gas technique.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11368/1708099
 Avviso

Registrazione in corso di verifica.
La registrazione di questo prodotto non è ancora stata validata in ArTS.

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 66
  • ???jsp.display-item.citation.isi??? ND
social impact