The effects ofredox-ageing on the temperature-programmed reduction and dynamic oxygen storage were investigated on two samples of Ce0.6Zr0.4O2 prepared under different synthesis conditions. It was observed that a high-temperature reduction/mild oxidation redox cycle can generate temperature-programmed reduction (TPR) profiles featuring a reduction peak at a temperature as low as 537 K. However, despite such favourable reduction behaviour, a strong deactivation of the oxygen storage is observed under dynamic conditions, indicating the limitations of the TPR method for investigation of oxygen storage.
A comparative study of oxygen storage capacity over Ce0.6Zr0.4O2 mixed oxides investigated by temperature-programmed reduction and dynamic OSC measurements
HICKEY, JAMES NEIL;FORNASIERO, Paolo;DI MONTE, ROBERTA;KASPAR, JAN;GRAZIANI, MAURO;
2001-01-01
Abstract
The effects ofredox-ageing on the temperature-programmed reduction and dynamic oxygen storage were investigated on two samples of Ce0.6Zr0.4O2 prepared under different synthesis conditions. It was observed that a high-temperature reduction/mild oxidation redox cycle can generate temperature-programmed reduction (TPR) profiles featuring a reduction peak at a temperature as low as 537 K. However, despite such favourable reduction behaviour, a strong deactivation of the oxygen storage is observed under dynamic conditions, indicating the limitations of the TPR method for investigation of oxygen storage.File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.