Two series of t-ZrO2 samples doped with 5 mol% of alien Sm, Gd, Mo, Mn and V cations were synthesized by wet impregnation and calcined at 600 °C or 1000 °C for 6 h, respectively. Structural (XRD) and spectroscopic (EPR, RS) characterization was completed by reducibility studies (TPR). Low-temperature NO adsorption, monitored by EPR, was investigated to find the link between structural properties of doped zirconia and activation modes of NO molecules. Relations between the chemical composition and dopant speciation, reducibility of the catalysts and the ways of NO adsorption were elucidated.
NO interaction with bare and transition-metal-ions-doped zirconia
FORNASIERO, Paolo;
2011-01-01
Abstract
Two series of t-ZrO2 samples doped with 5 mol% of alien Sm, Gd, Mo, Mn and V cations were synthesized by wet impregnation and calcined at 600 °C or 1000 °C for 6 h, respectively. Structural (XRD) and spectroscopic (EPR, RS) characterization was completed by reducibility studies (TPR). Low-temperature NO adsorption, monitored by EPR, was investigated to find the link between structural properties of doped zirconia and activation modes of NO molecules. Relations between the chemical composition and dopant speciation, reducibility of the catalysts and the ways of NO adsorption were elucidated.File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.