EnglishThe aim of the study was to evaluate the reaction exothermia of 2 relining resins for temporary crowns. The resins used were Duralay, a methacrylate-based resin, and Protemp II, a bisacrylic resin. METHODS: The coronal parts of an adult molar and of an impacted one were used. Abutments were obtained from the crowns, while the radicular part was sectioned in order to insert a thermocouple into the pulpal chamber. During the experiment the tooth with the polymerising resin was put into an oral cavity simulator to keep a constant temperature. The thermal increase during polymerisation of the 2 resins was recorded for 6 minutes at 5 seconds intervals and with 1 and 2.5 mm dentin thickness (n = 10). Data were statistically analysed by variance analysis with Scheffe test. RESULTS: The intrapulpal thermal increase was significantly higher in relation to the type of resin (Duralay p < 0.0001), thickness (1 mm p < 0.0001) and type of dentin (young dentin p < 00001). CONCLUSIONS: In order to protect the pulp, during the direct relining of a temporary crown, it is recommendable to choose the best combination among resin, type of dentin and its residual thickness, besides adequate cooling techniques.
| Titolo: | Reaction exothermia of 2 relining resins for temporary crowns. | |
| Autori: | ||
| Data di pubblicazione: | 2005 | |
| Rivista: | ||
| Abstract: | The aim of the study was to evaluate the reaction exothermia of 2 relining resins for temporary crowns. The resins used were Duralay, a methacrylate-based resin, and Protemp II, a bisacrylic resin. METHODS: The coronal parts of an adult molar and of an impacted one were used. Abutments were obtained from the crowns, while the radicular part was sectioned in order to insert a thermocouple into the pulpal chamber. During the experiment the tooth with the polymerising resin was put into an oral cavity simulator to keep a constant temperature. The thermal increase during polymerisation of the 2 resins was recorded for 6 minutes at 5 seconds intervals and with 1 and 2.5 mm dentin thickness (n = 10). Data were statistically analysed by variance analysis with Scheffe test. RESULTS: The intrapulpal thermal increase was significantly higher in relation to the type of resin (Duralay p < 0.0001), thickness (1 mm p < 0.0001) and type of dentin (young dentin p < 00001). CONCLUSIONS: In order to protect the pulp, during the direct relining of a temporary crown, it is recommendable to choose the best combination among resin, type of dentin and its residual thickness, besides adequate cooling techniques. | |
| Handle: | http://hdl.handle.net/11368/2753955 | |
| URL: | http://www.ncbi.nlm.nih.gov/pubmed/?term=Reaction+exothermia+of+2+relining+resins+for+temporary+crowns | |
| Appare nelle tipologie: | 1.1 Articolo in Rivista |
File in questo prodotto:
http://hdl.handle.net/11368/2753955