EnglishThe mechanism of formation of Pt@SiO2 as a model of core–shell nanoparticles via water-in-oil reverse microemulsions was studied in detail. By controlling the time of growth of Pt precursors, Pt(OH)x, after hydrolysis in NH3 aq. before adding SiO2 precursor (TEOS), Pt nanoparticles with a narrow size distribution were produced, from ultrafine metal nanoparticles (<1 nm) to 6 nm nanocrystals. Separately, the thickness of SiO2 was controllably synthesized from 1 to 15 nm to yield different Pt@SiO2 materials. The Pt@SiO2 core–shell catalysts exhibited a higher rate of CO oxidation by one order of magnitude with a positive order regarding CO pressure. The SiO2 shell did not perturb the Pt chemical nature, but it provided different coverage of CO in steady-state CO oxidation.
| Titolo: | Design of a core–shell Pt–SiO2 catalyst in a reverse microemulsion system: Distinctive kinetics on CO oxidation at low temperature |
| Autori: | |
| Data di pubblicazione: | 2016 |
| Rivista: | |
| Abstract: | The mechanism of formation of Pt@SiO2 as a model of core–shell nanoparticles via water-in-oil reverse microemulsions was studied in detail. By controlling the time of growth of Pt precursors, Pt(OH)x, after hydrolysis in NH3 aq. before adding SiO2 precursor (TEOS), Pt nanoparticles with a narrow size distribution were produced, from ultrafine metal nanoparticles (<1 nm) to 6 nm nanocrystals. Separately, the thickness of SiO2 was controllably synthesized from 1 to 15 nm to yield different Pt@SiO2 materials. The Pt@SiO2 core–shell catalysts exhibited a higher rate of CO oxidation by one order of magnitude with a positive order regarding CO pressure. The SiO2 shell did not perturb the Pt chemical nature, but it provided different coverage of CO in steady-state CO oxidation. |
| Handle: | http://hdl.handle.net/11368/2891896 |
| Digital Object Identifier (DOI): | 10.1016/j.jcat.2016.06.002 |
| URL: | http://www.sciencedirect.com/science/article/pii/S0021951716300823 |
| Appare nelle tipologie: | 1.1 Articolo in Rivista |
File in questo prodotto:
| File | Descrizione | Tipologia | Licenza | |
|---|---|---|---|---|
| 1-s2.0-S0021951716300823-main.pdf | main text | N/A | Digital Rights Management non definito | Administrator Richiedi una copia |
| mmc1.pdf | Supplementary data | Altro | Digital Rights Management non definito | Administrator Richiedi una copia |
http://hdl.handle.net/11368/2891896