The combination of Low-Field NMR relaxometry (LF-NMR) and rheological analyses was used to investigate the kinetics of aging and structural evolution of salt-free aqueous Laponite dispersions with concentrations ranging from 0.33 to 2.00 wt%. The examination of LF-NMR results reveals that the rate of nanoclay delamination increases with increasing Laponite concentration while its degree decreases. Furthermore, the LF-NMR results were interpreted together with rheological results to assess the kinetics of processes occurring on different length scales reflecting on the time evolution of the three-dimensional structure. The structural evolution is described by the definition and comparison of three different characteristic times. The LF-NMR decay time (tr) designates the time required for Laponite delamination. The induction time (ti) indicates when interparticle edge-face interactions become effective enough for incipient networking. The gelation time (tg) corresponds to sufficiently high degree of interparticle connectivity for the development of a macroscopic gel behavior. The comparison of ti and tg, on one hand, and tr, on the other hand, allows to conclude that for low concentration Laponite dispersions nanoclay delamination is a prerequisite for the formation of the new dispersion structure with a macroscopic gel behavior. Interestingly, the development of the new structure, based on orientation of clay disks into edge-to-face pattern and mutual interparticle attractive interactions, starts when the delamination process is still running.

Structural evolution of salt-free aqueous Laponite dispersions: A study based on low-field NMR relaxometry and rheological investigations

Lapasin R.
;
Grassi M.;Abrami M.;Sebenik U.
2020-01-01

Abstract

The combination of Low-Field NMR relaxometry (LF-NMR) and rheological analyses was used to investigate the kinetics of aging and structural evolution of salt-free aqueous Laponite dispersions with concentrations ranging from 0.33 to 2.00 wt%. The examination of LF-NMR results reveals that the rate of nanoclay delamination increases with increasing Laponite concentration while its degree decreases. Furthermore, the LF-NMR results were interpreted together with rheological results to assess the kinetics of processes occurring on different length scales reflecting on the time evolution of the three-dimensional structure. The structural evolution is described by the definition and comparison of three different characteristic times. The LF-NMR decay time (tr) designates the time required for Laponite delamination. The induction time (ti) indicates when interparticle edge-face interactions become effective enough for incipient networking. The gelation time (tg) corresponds to sufficiently high degree of interparticle connectivity for the development of a macroscopic gel behavior. The comparison of ti and tg, on one hand, and tr, on the other hand, allows to conclude that for low concentration Laponite dispersions nanoclay delamination is a prerequisite for the formation of the new dispersion structure with a macroscopic gel behavior. Interestingly, the development of the new structure, based on orientation of clay disks into edge-to-face pattern and mutual interparticle attractive interactions, starts when the delamination process is still running.
2020
Pubblicato
https://www.sciencedirect.com/science/article/pii/S0927775720307196
File in questo prodotto:
File Dimensione Formato  
CollSurfA 2020.pdf

Accesso chiuso

Tipologia: Documento in Versione Editoriale
Licenza: Copyright Editore
Dimensione 1.34 MB
Formato Adobe PDF
1.34 MB Adobe PDF   Visualizza/Apri   Richiedi una copia
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11368/2977713
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 5
  • ???jsp.display-item.citation.isi??? 5
social impact