Carbon nanodots, a class of carbon nano-allotropes, have been synthesized through different routes and methods from a wide range of precursors. The selected precursor, synthetic method, and conditions can strongly alter the physicochemical properties of the resulting material and their intended applications. Herein, carbon nanodots (CNDs) have been synthesized from D- glucose by combining pyrolysis and chemical oxidation methods. The effect of the pyrolysis temperature, equivalents of oxidizing agent, and refluxing time were studied on the product and quantum yield. In the optimum conditions (pyrolysis temperature of 300 degrees C, 4.41 equiv of H2O2, 90 min of reflux) CNDs were obtained with 40% and 3.6% of product and quantum yields, respectively. The obtained CNDs are negatively charged (zeta-potential = -32 mV), excellently dispersed in water, with average diameter of 2.2 nm. Furthermore, ammonium hydroxide (NH4OH) was introduced as dehydrating and/or passivation agent during CNDs synthesis resulting in significant improvement of both product and quantum yields of about 1.5 and 3.76-fold, respectively. The synthesized CNDs showed a broad spectrum of antibacterial activities toward different Gram-positive and Gram-negative bacteria strains. Both synthesized CNDs caused highly colony forming unit reduction (CFU), ranging from 98% to 99.99% for most of the tested bacterial strains. However, CNDs synthesized in the absence of NH4OH, due to a negatively charged surface enriched in oxygenated groups, performed better in zone inhibition and minimum inhibitory concentration. The elevated antibacterial activity of high-oxygen-containing carbon nanodots is directly correlated to their ROS formation ability.

Broad-Spectrum Antibacterial Activity of Synthesized Carbon Nanodots from d-Glucose

Misia, Giuseppe;Prato, Maurizio;
2022-01-01

Abstract

Carbon nanodots, a class of carbon nano-allotropes, have been synthesized through different routes and methods from a wide range of precursors. The selected precursor, synthetic method, and conditions can strongly alter the physicochemical properties of the resulting material and their intended applications. Herein, carbon nanodots (CNDs) have been synthesized from D- glucose by combining pyrolysis and chemical oxidation methods. The effect of the pyrolysis temperature, equivalents of oxidizing agent, and refluxing time were studied on the product and quantum yield. In the optimum conditions (pyrolysis temperature of 300 degrees C, 4.41 equiv of H2O2, 90 min of reflux) CNDs were obtained with 40% and 3.6% of product and quantum yields, respectively. The obtained CNDs are negatively charged (zeta-potential = -32 mV), excellently dispersed in water, with average diameter of 2.2 nm. Furthermore, ammonium hydroxide (NH4OH) was introduced as dehydrating and/or passivation agent during CNDs synthesis resulting in significant improvement of both product and quantum yields of about 1.5 and 3.76-fold, respectively. The synthesized CNDs showed a broad spectrum of antibacterial activities toward different Gram-positive and Gram-negative bacteria strains. Both synthesized CNDs caused highly colony forming unit reduction (CFU), ranging from 98% to 99.99% for most of the tested bacterial strains. However, CNDs synthesized in the absence of NH4OH, due to a negatively charged surface enriched in oxygenated groups, performed better in zone inhibition and minimum inhibitory concentration. The elevated antibacterial activity of high-oxygen-containing carbon nanodots is directly correlated to their ROS formation ability.
File in questo prodotto:
File Dimensione Formato  
acsabm.2c00590.pdf

Accesso chiuso

Descrizione: Articolo scientico
Tipologia: Documento in Versione Editoriale
Licenza: Copyright Editore
Dimensione 8.35 MB
Formato Adobe PDF
8.35 MB Adobe PDF   Visualizza/Apri   Richiedi una copia
mt2c00590_si_001.pdf

Accesso chiuso

Descrizione: supporting material
Tipologia: Altro materiale allegato
Licenza: Copyright Editore
Dimensione 393.1 kB
Formato Adobe PDF
393.1 kB Adobe PDF   Visualizza/Apri   Richiedi una copia
acsabm.2c00590-Post_print.pdf

Open Access dal 14/09/2023

Tipologia: Bozza finale post-referaggio (post-print)
Licenza: Digital Rights Management non definito
Dimensione 8.34 MB
Formato Adobe PDF
8.34 MB Adobe PDF Visualizza/Apri
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11368/3056661
Citazioni
  • ???jsp.display-item.citation.pmc??? 1
  • Scopus 10
  • ???jsp.display-item.citation.isi??? 11
social impact