In the present investigation, Cu2O-based composites were successfully prepared througha multistep method where cubic Cu2O nanoparticles (CU Cu2O) have been grown on Reduced Graphene Oxide (RGO) nanosheets. The structural and morphological properties of the materials have been studied through a comprehensive characterization, confirming the coexistence of crystalline Cu2O and RGO. Microscopical imaging revealed the intimate contact between the two materials, affecting the size and the distribution of Cu2O nanoparticles on the support. The features of the improved morphology strongly affected the electrochemical behavior of the composites, increasing the activity and the faradaic efficiencies towards the electrochemical CO2 reduction reaction process. CU Cu2O/RGO 2:1 composite displayed selective CO formation over H2, with higher currents compared to pristine Cu2O (−0.34 mA/cm2 for Cu2O and −0.64 mA/cm2 for CU Cu2O/RGO 2:1 at the voltage of −0.8 vs. RHE and in a CO2 atmosphere) and a faradaic efficiency of 50% at −0.9 V vs. RHE. This composition exhibited significantly higher CO production compared to the pristine materials, indicating a favorable *CO intermediate pathway even at lower voltages. The systematic investigation on the effects of nanostructuration on composition, morphology and catalytic behavior is a valuable solution for the formation of effective interphases for the promotion of catalytic properties providing crucial insights for future catalysts design and applications.
CO2 Electroreduction by Engineering the Cu2O/RGO Interphase
Bisetto, Matteo
;Montini, Tiziano;Fornasiero, Paolo
2024-01-01
Abstract
In the present investigation, Cu2O-based composites were successfully prepared througha multistep method where cubic Cu2O nanoparticles (CU Cu2O) have been grown on Reduced Graphene Oxide (RGO) nanosheets. The structural and morphological properties of the materials have been studied through a comprehensive characterization, confirming the coexistence of crystalline Cu2O and RGO. Microscopical imaging revealed the intimate contact between the two materials, affecting the size and the distribution of Cu2O nanoparticles on the support. The features of the improved morphology strongly affected the electrochemical behavior of the composites, increasing the activity and the faradaic efficiencies towards the electrochemical CO2 reduction reaction process. CU Cu2O/RGO 2:1 composite displayed selective CO formation over H2, with higher currents compared to pristine Cu2O (−0.34 mA/cm2 for Cu2O and −0.64 mA/cm2 for CU Cu2O/RGO 2:1 at the voltage of −0.8 vs. RHE and in a CO2 atmosphere) and a faradaic efficiency of 50% at −0.9 V vs. RHE. This composition exhibited significantly higher CO production compared to the pristine materials, indicating a favorable *CO intermediate pathway even at lower voltages. The systematic investigation on the effects of nanostructuration on composition, morphology and catalytic behavior is a valuable solution for the formation of effective interphases for the promotion of catalytic properties providing crucial insights for future catalysts design and applications.File | Dimensione | Formato | |
---|---|---|---|
catalysts-14-00412-v2.pdf
accesso aperto
Descrizione: manoscritto
Tipologia:
Documento in Versione Editoriale
Licenza:
Creative commons
Dimensione
3.07 MB
Formato
Adobe PDF
|
3.07 MB | Adobe PDF | Visualizza/Apri |
catalysts-3049970-supplementary xml.pdf
accesso aperto
Descrizione: Supporting material
Tipologia:
Altro materiale allegato
Licenza:
Creative commons
Dimensione
3.16 MB
Formato
Adobe PDF
|
3.16 MB | Adobe PDF | Visualizza/Apri |
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.